Influence of double calcination-milling route on the structural and microstructural properties of lead-free K0.5Na0.5NbO3 (KNN) ceramics.

Norni Hidayawati, Mat Daud and Dzetty Soraya, Abdul Aziz and Idza Riati, Ibrahim and Dayang Salyani, Abang Mahmod and Amir Azam, Khan and Nor Amalina, Ahmad (2023) Influence of double calcination-milling route on the structural and microstructural properties of lead-free K0.5Na0.5NbO3 (KNN) ceramics. Jurnal Teknologi, 85 (3). pp. 75-81. ISSN 2180-3722

[img] PDF
INFLUENCE OF DOUBLE - Copy.pdf

Download (108kB)
Official URL: https://journals.utm.my/jurnalteknologi/article/vi...

Abstract

Potassium sodium niobate (KNN) has always beenone of the most potential candidates to replace lead-based piezoelectric ceramics due to its strong piezoelectric properties and environmentally friendly composition. A strong piezoelectric property is constantly influenced by the sample's densification as well as its microstructural characteristics. One of the current main issues with this KNN lead-free piezoelectric material is the difficulty in creating high-density samples by conventional preparation and sintering. Thus, KNN lead-free ceramics were synthesised using an improved solid-state method by introducing the double calcination-milling route to this process. The outcome demonstrates that, despite the presence of additional KNN secondary phases, the double calcination-milling approach contributed to the early creation of the KNN phase. When sintered pellets are subjectedto adouble calcination milling process, the XRD pattern revealed that the main peaks of the sample are indexed to orthorhombic K0.5Na0.5NbO3.The double calcination KNN pellet havea relative density of 90% densificationwhich is slightly higher than that of single calcination KNN pellet which shows 88% densification

Item Type: Article
Uncontrolled Keywords: Potassium Sodium Niobate, piezoelectric ceramic, double calcination, solid state method, sintering.
Subjects: Q Science > QC Physics
Divisions: Academic Faculties, Institutes and Centres > Centre for Pre-University Studies
Faculties, Institutes, Centres > Centre for Pre-University Studies
Academic Faculties, Institutes and Centres > Centre for Pre-University Studies
Depositing User: Mat Daud
Date Deposited: 05 May 2023 02:57
Last Modified: 05 May 2023 02:57
URI: http://ir.unimas.my/id/eprint/41773

Actions (For repository members only: login required)

View Item View Item