A Study on Microwave Absorption Properties of Carbon Black and Ni0.6Zn0.4Fe2O4 Nanocomposites by Tuning the Matching-Absorbing Layer Structures

Idza Riati, Ibrahim and Khamirul Amin, Matori and Ismayadi, Ismail and Zaiki, Awang and Siti Nor Ain, Rusly and Rodziah, Nazlan and Fadzidah, Mohd Idris and Muhammad Misbah, Muhammad Zulkimi and Nor Hapishah, Abdullah and Muhammad Syazwan, Mustaffa and Farah Nabilah, Shafiee and Mehmet, Ertugrul (2020) A Study on Microwave Absorption Properties of Carbon Black and Ni0.6Zn0.4Fe2O4 Nanocomposites by Tuning the Matching-Absorbing Layer Structures. Scientific Reports, 10 (3135). pp. 1-14.

[img] PDF
Idza Riati Ibrahim.pdf

Download (470kB)
Official URL: https://www.nature.com/articles/s41598-020-60107-1

Abstract

Microwave absorption properties were systematically studied for double-layer carbon black/epoxy resin (CB) and Ni0.6Zn0.4Fe2O4/epoxy resin (F) nanocomposites in the frequency range of 8 to 18 GHz. The Ni0.6Zn0.4Fe2O4 nanoparticles were synthesized via high energy ball milling with subsequent sintering while carbon black was commercially purchased. The materials were later incorporated into epoxy resin to fabricate double-layer composite structures with total thicknesses of 2 and 3 mm. The CB1/F1, in which carbon black as matching and ferrite as absorbing layer with each thickness of 1 mm, showed the highest microwave absorption of more than 99.9%, with minimum reflection loss of −33.8 dB but with an absorption bandwidth of only 2.7 GHz. Double layer absorbers with F1/CB1(ferrite as matching and carbon black as absorbing layer with each thickness of 1 mm) structure showed the best microwave absorption performance in which more than 99% microwave energy were absorbed, with promising minimum reflection loss of −24.0 dB, along with a wider bandwidth of 4.8 GHz and yet with a reduced thickness of only 2 mm.

Item Type: Article
Uncontrolled Keywords: Microwave absorption properties, carbon black/epoxy resin (CB), Ni0.6Zn0.4Fe2O4/epoxy resin (F), unimas, university, universiti, Borneo, Malaysia, Sarawak, Kuching, Samarahan, ipta, education, research, Universiti Malaysia Sarawak
Subjects: Q Science > Q Science (General)
Divisions: Academic Faculties, Institutes and Centres > Centre for Pre-University Studies
Faculties, Institutes, Centres > Centre for Pre-University Studies
Academic Faculties, Institutes and Centres > Centre for Pre-University Studies
Depositing User: Tuah
Date Deposited: 21 Sep 2020 07:40
Last Modified: 31 Mar 2021 03:50
URI: http://ir.unimas.my/id/eprint/31872

Actions (For repository members only: login required)

View Item View Item